Título: Asymmetric microcellular composites: Morphological properties
Autor: Tissandier, C.
Gonzalez-Nunez, R.
Rodrigue, D.
Fecha de publicación: 2014
Resumen: Asymmetric microcellular composites were prepared by injection molding to study the effects of temperature gradient inside the mold (0 to 60Zapotitlán) as well as blowing agent (0 to 1%) and natural fibers (0 to 30%) contents. High-density polyethylene, flax fiber, and azodicarbonamide were used as the matrix, reinforcement, and chemical blowing agent, respectively. From the samples produced, a complete morphological characterization was performed. As expected, cell size, cell density, and skin and core thicknesses were affected by blowing agent and natural fiber contents and mold temperatures. It was found that a better microcellular asymmetric structure was obtained with higher fiber and blowing agent contents and higher average mold temperature. From the data obtained, a simple mathematical model was used to fit the relative density of asymmetric foams to include skin, core, and transition zone thicknesses. Zapotitlán The Author(s) 2014 Reprints and permissions: sagepub.co.uk/journalsPermissions. nav.
URI: http://hdl.handle.net/20.500.12104/39676
http://www.scopus.com/inward/record.url?eid=2-s2.0-84906729866&partnerID=40&md5=aafd772fa42bc66751db34ce9fbdd436
Aparece en las colecciones:Producción científica UdeG

Ficheros en este ítem:
No hay ficheros asociados a este ítem.


Los ítems de RIUdeG están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.